Compression-molding-grade PVDF
PHYSICAL PROPERTIE
| Item | Unit | Index | Test Method / Standards |
| Melt Mass Flow Rate | g/10min | 1.0〜6.0 | ASTM D1238、GB/T 3682 (230℃，12.5kg) |
| Tensile Strength | MPa | ≥35.0 | ASTM D638、GB/T 1040.1 |
| Elongation at Break | ％ | ≥200 | ASTM D638、GB/T 1040.1 |
| Yield Tensile Strength | MPa | ≥34.0 | ASTM D638、GB/T 1040.1 |
| Yield Elongation | ％ | ≥15 | ASTM D638、GB/T 1040.1 |
| Standard Relative Density | / | 1.75〜1.79 | ASTM D792、GB/T 1033.1 |
| Hardness(Shore D) | / | 70〜80 | ASTM D2240、GB/T 2411 |
| Melting Point | ℃ | 160〜170 | ASTM D3418 |
Product Description
This product is a homopolymer of vinylidene fluoride with a low melt flow rate and high melt viscosity. This resin is resistant to most chemical media and possesses excellent heat resistance, high mechanical strength, high abrasion resistance, UV resistance, and radiation resistance.
Application
It is mainly used for lining pumps, valves, pipe fittings and equipment of various specifications, as well as other parts that can be processed by molding.
Packaging
- Packed in polyethylene plastic bags, and then sealed in outer packaging bags, each bag contains a net weight of 25 kg.
Transportation & Storage
Transportation: Transport as non-dangerous goods. Avoid heat, moisture, or severe vibration during transportation.
Storage: It should be stored in a clean and dry environment at 5~30℃ to prevent impurities such as dust and water vapor from mixing in.
Attention
Avoid processing or using at temperatures above 370℃ to prevent decomposition and the generation of toxic gases.